简介:GB/T15579.5-2005《弧焊设备安全要求第五部分:送丝装置》和GB/T15579.7-2005《弧焊设备安全要求第七部分:焊炬(枪)》(以下简称新标准)已于2005年12月1日正式实施。自新标准实施之日起.JB/T9533-1999《焊机送丝装置:技术条件》、JB/T9526-1999《TIG焊焊炬技术条件》和JB/T9532-1999《MIG/MAG焊焊枪技术条件》(以下简称旧标准)废止。
简介:ThediffusionbondingofAZ3\BMgalloyandQ235steelwasinvestigatedwithaZn-5AIalloyasinterlayerandunderdifferentholdingtimerangingfrom3to1200s.Themicrostructureandphasecompositionsofbondedjointswerecharacterizedbyscanningelectronmicroscopy(SEM),energydispersivespectrometer(EDS)andX-raydiffraction(XRD)methods.TheshearstrengthofMgalloy/steeljointswasmeasuredbytensiletester.Itwasfoundthatthemicrostructureofbondedjointsevolveddramaticallyalongwiththeprolongationofholdingtime.Undertheholdingtimeof3s,themainpartofjointwascomposedofMgZn2phaseanddispersedAl-richsolidsolutionparticles.Whenincreasedtheholdingtimemorethan60s,theexcessivesolutionofAZ3\Bintotheinterfacialreactionarealedtotheformationofcoarsephaseandeutecticmicrostructure,andalsothecomplexFe-AlandMg-Al-ZnIMCsattransitionlayerclosedtoQ235steelside.Accordingtothetensiletestingcharacterizations,thejointsobtainedunderholdingtimeof3sexhibitedthebestshearstrengthof84MPa,andthefractureoccurredattheintermediarypartofjointwheretheflexibleAl-richsolidsolutionparticlescouldhelptoimpedethemicrocrackpropagations.Withprolongingtheholdingtimeto600s,theshearstrengthofjointswasdeterioratedenormouslyandthefracturepositionwasshiftedtothetransitionlayerpartclosedtoQ235steel.