Cr2O3-formingferriticstainlesssteelshavebeenwidelyexploredasintermediatetemperaturesolidoxidefuelcells（SOFCs）interconnects.However,theevaporationofchromiascalemightmigratetoandpoisonthecathode,leadingtodegradationofthecellperformance.Inthisstudy,Ni-Co-Fe-Pcoatingsweredepositedontheferriticstainlesssteelbymeansofacost-effectivetechniqueofelectrolessmethod.Theyareexpectedtobeconvertedinto（Ni,Co,Fe）3O4spinelwithahighelectricalconductivityandCTEmatchwithstainlesssteel,whichcanblocktheevaporationofchromiaformedonsteelsubstrateexposedtothecathodeenvironmentoftheSOFC.TheeffectsofpH,massratioofFeSO4/（FeSO4+NiSO4+CoSO4）andtemperatureofsolutiononthedepositionrate,compositions,surfacemorphologiesandstructuresoftheNi-Co-Fe-Pcoatingswereinvestigated.TheresultsindicatedthatthedepositionrateincreasedwithincreasingpHwhenpHwaslowerthan9andthenreducedwhenpHwashigherthan9.Thedepositionrateincreasedwithincreasingtemperaturewhentemperaturewaslowerthan80℃andthendecreasedwhentemperaturewashigherthan80℃.ThedepositionratedecreasedwiththeincreaseinmassratioofFeSO4/（NiSO4+CoSO4+FeSO4）.ThecoatingsconsistedofNi,Co,FeandP.Thephasestructureofthecoatingwasamorphous.