简介：本文采用磁粉、X射线、CT和超声等无损检测和金相分析等方法对40CrNi2Si2,MoVA钢制零件的磁痕显示进行了系统分析。研究认为，40CrNi2Si2MoVA钢制零件的磁痕显示为显微成分沿变形方向偏析导致的马氏体转变点Ms差异所致。显微成分偏析是钢锭结晶过程中不可避免的，但可通过优化熔炼工艺参数降低显微偏析的程度。本文还分析了四种磁痕显示的类型及其判别方法。

简介：起落架40CrNi2Si2MoVA钢螺桩在安装一段时间后发生了断裂。为确定螺桩断裂的原因，对断裂螺桩断口宏微观形貌、断裂螺桩及对比件的氢含量、材料的性能以及表面损伤等因素进行了检查，并对电镀工艺进行了评定。结果表明，裂纹主要起源于第一螺纹根部的机械损伤部位，源区以沿晶断裂特征为主，断裂件含氢量较高。综合分析认为。螺桩断裂性质为氢致延迟断裂，表面机械损伤对氢吸收和扩散的促进作用和40CrNi2Si2MoVA钢材料高强度所致的高氢脆敏感性是导致断裂的主要原因。

简介：Nb-24Ti-18Si-2Al-2Hf-4CrandNb-24Ti-18Si-2Al-2Hf-8Cralloyswerepreparedbyarcmeltinginawater-cooledcrucibleunderargonatmosphere.Microstructuralcharacteristicsandoxidationresistanceofthealloysat1250℃wereinvestigated.Theresultsshowthat,whentheCrcontentis4at%,themicrostructuresconsistof(Nb,Ti)_(ss)andNb_5Si_3;asCrcontentincreasesto8at%,C14LavesphaseCr_2Nbisformed.Theisothermaloxidationtestsshowthattheoxidationkineticsofthetwoalloysfollowsimilarfeatures.Theweightgainsofthetwoalloysafteroxidationat1250℃for100hare235.61and198.50mg·cm~(-2),respectively.Duringoxidation,SiO_2,TiO_2,Nb_2O_5andCrNbO_4areformedatfirst.Then,Ti_2Nb_(10)O_(29)isformedafteroxidationfor20minandbeginstochangeintoTiNb_2O_7astheoxidationproceeds.SiO_2isformedassolidstateatfirstbutlaterevolvesintoglassystatetoimprovethecohesionofthescale.Afteroxidationfor100h,oxidationproductsconsistofSiO_2,TiNb_2O_7,Nb_2O_5andCrNbO_4.

简介：60Si2MnA钢制弹条进行疲劳寿命试验,未达到规定的疲劳寿命时发生断裂。通过断口宏微观观察、金相组织检查、硬度检测、化学成分检测,对弹条断裂原因进行了分析。结果表明：弹条断裂性质为弯曲-扭转疲劳断裂,其断口明显分成疲劳源区、扩展区和瞬断区3个区域,疲劳源区位于弹条表面;弹条断裂主要原因与弹条表面质量差有关,弹条表层存在脱碳层导致弹条抗疲劳性能降低,也是弹条疲劳断裂的又一原因。

简介：采用光学显微镜和场发射扫描电镜,研究超声波对原位Mg2Si/Al复合材料中初生Mg2Si形态的影响。研究结果表明:超声波处理使初生Mg2Si的晶粒尺寸从150μm降低到20μm,初生Mg2Si形态发生改变。在二维形貌中,未实施超声波振动处理的初生Mg2Si晶粒生长为含有空腔的粗大颗粒,共晶组织生长于其中,相应的三维形态为含有漏斗状空腔的八面体和十四面体。超声波处理后的初生Mg2Si晶粒变成细小、实心三维形态的颗粒,颗粒棱角已发生钝化效应。

简介：

简介：研究Al-Mg-Si合金晶界组成相（Al-Mg2Si及Al-Mg2Si-Si）间的电化学行为和动态电化学耦合行为,提出Al-Mg-Si合金的晶间腐蚀机理。研究表明,晶界Si的电位比其边缘Al基体的正,在整个腐蚀过程中作为阴极导致其边缘Al基体的阳极溶解;晶界Mg2Si的电位比其边缘Al基体的负,在腐蚀初期作为阳极发生阳极溶解,然而由于Mg2Si中活性较高的元素Mg的优先溶解,不活泼元素Si的富集,致使Mg2Si电位正移,甚至与其边缘Al基体发生极性转换,导致其边缘Al基体的阳极溶解。当n（Mg）/n（Si）〈1.73时,随着腐蚀的进行,合金晶界同时会有Mg2Si析出相和Si粒子,腐蚀首先萌生于Mg2Si相和Si边缘的无沉淀带,而后,Si粒子一方面导致其边缘无沉淀带严重的阳极溶解,另一方面加速Mg2Si和晶界无沉淀带的极性转换,从而促使腐蚀沿晶界Si粒子及Mg2Si粒子边缘向无沉淀带发展。

简介：利用扫描电子显微镜、能谱仪、光学金相显微镜、光谱仪等仪器,对40Mn2锻造磨球以及锻造坯料进行组织分析和化学成分测定,探讨了生产过程中锻造磨球出现裂纹和心部孔洞等缺陷的主要原因。结果表明：锻造坯料中存在较严重的带状组织和缩孔、夹杂等缺陷;同时锻造磨球淬火过程中热处理工艺参数不合理,形成粗大的魏氏组织;建议在冶炼过程中添加去渣剂,在轧制生产过程后增加均匀化退火处理,在锻造生产中调整加热、冷却条件以避开魏氏组织生成区域。

简介：

简介：为改善La-Mg-Ni系A2B7型合金的电化学贮氢性能，在合金中添加一定量的Si元素，通过真空熔炼及退火处理的方法制备La0.8Mg0.2Ni3.3Co0.2Six（x=0-0.2）电极合金。研究Si元素的添加对合金结构及电化学贮氢性能的影响。结果表明，铸态及退火态合金均为多相结构，分别为Ce2Ni7型的（La,Mg）2Ni7相和CaCu5型的LaNi5相以及少量的残余相LaNi3。Si元素的添加没有改变合金的主相，但使得合金中的（La,Mg）2Ni7相减少而LaNi5相增加。添加Si显著地影响了合金的电化学性能。随着Si含量的增加，铸态及退火态合金的放电容量逐步降低，但循环稳定性却随着Si含量的增加而增强。此外，合金电极的高倍率放电性能、极限电流密度、氢扩散系数以及电化学交流阻抗谱的测试均表明合金的电化学动力学性能随着Si含量的增加先增加而后减小。

简介：采用原位电阻率测试和透射电镜观察研究Al—0．96Mg2Si合金的析出行为及其对电阻率的影响。发现峰值时效的析出相包括β＂和β＇，而他们的比例随着时效温度和时间的改变而变化。合金在175℃峰值时效内的析出相主要是针状β＂相（也包括pre-β＂）。这些析出相会随着时效时间的延长而长大，但是进一步延长时效时间至超出峰值时效时间后，析出相的尺寸变化并不显著。合金电导率的变化规律与之类似。合金硬度峰值时效后，继续时效很长一段时间硬度变化都不显著。由于温度是影响β＂β’比的主要因素，因此时效温度也是影响电阻率的主要因素。时效温度越高β＂／β’的比值越小，△p下降的速度就越快。硬度也随着该比值的减小而降低。通过对透射电镜照片分析获得析出相的分布参数，建立了析出相与电阻率之间的半定量关系式。

简介：以MoO3粉、Mo粉、Si粉及Al粉为原料,采用机械合金化法合成了纳米Mo5Si3-20%Al2O3(质量分数)复合粉体。采用XRD、SEM、TEM和DTA等对复合粉体在球磨过程中结构变化进行了研究。结果表明:球磨10h后合成的Mo5Si3-20%Al2O3复合粉体,反应以爆炸模式进行。球磨30h后,Mo5Si3和Al2O3的晶粒尺寸分别为36.3nm和21.9nm。随着球磨时间的延长,Mo5Si3和Al2O3的晶粒尺寸变小,衍射峰宽化程度降低。DTA和XRD分析结果表明,复合粉体具有好的热稳定性,球磨30h后再在1000℃退火1h后复合粉体没有发生物相转变。更多还原

简介：TiO2nanoparticleswithdifferentphasesarepreparedbyhydrolysisoftitaniumtetrabutoxideinthepresenceofHCl.ThecompositionandmicrostructureoftheresultingsamplesarestudiedbyXRDandTEM.TheseresultsshowthattherangeofparticlesizeofTiO2isfrom20to30nm.ThemechanismofTiO2photocatalysisreactionhasbeendiscussedextensively.PhotocatalyticactivitiesofnanometerTiO2arealsoevaluatedbydegradationofthecrystalvioletsolution.ExperimentalresultsindicatethatthesynergisticactionofH2O2andultrasonicwavegreatlyenhancesphoto-catalyticreactionofTiO2.

简介：Iron(Ⅲ)-dopednanostructureTiO2-coatedSiO2(TiO2/SiO2)particleswerepreparedusingthelayer-by-layeras-semblytechniqueandtheirphotocatalyticpropertywasstudied.TiO2colloidsweresynthesizedemployingthesol-gelmethodwithTiCl4asaprecursor.ThesampleswerecharacterizedbyFouriertransforminfraredspectroscopy(FTIR),SEM,EDS,XPS,andXRD.TheexperimentalresultsshowthatTiO2nanopowdersonthesurfaceofSiO2particlesarewelldistributed,theamountofTiO2isincreasedwiththeaddingofcoatinglayers,thepureanatase-TiO2coatinglayersaresynthesizedat500°C,andthephotocatalyticactivityofFe3+-dopedTiO2/SiO2ishigherthanthatofundopedTiO2/SiO2.

简介：ＥｌｅｃｔｒｏｃｒｙｓｔａｌｌｉｚａｔｉｏｎＭｅｃｈａｎｉｓｍｏｆＴｕｎｇｓｔｅｎｉｎＭｏｌｔｅｎＫＦ－Ｂ＿２Ｏ＿３－Ｋ＿２ＷＯ＿４ＷｅｎＺｈｅｎｈｕａｎａｎｄＬｉＧｕｏｘｕｎ文振环，李国勋（ＧｅｎｅｒａｌＲｅｓｅａｒｃｈＩｎｓｔｉｉｕｔｅｆｏｒＮｏ...

简介：在高能超声场下利用熔体原位反应制备TiB2/Al-30Si复合材料;利用XRD、SEM及干磨损试验研究此复合材料的显微组织和磨损性能。结果表明：在高能超声场作用下,原位TiB2颗粒在铝基体中分布均匀,形貌为圆形或四边形,尺寸在0.1-1.5μm之间。初生硅的形貌为四边形,平均尺寸为10μm。随着高能超声功率的增加,Al-30Si基体合金及TiB2/Al-30Si复合材料的硬度明显提高;特别是当超声功率为1.2kW时,复合材料的硬度达到412MPa,是基体合金的1.3倍。复合材料的磨损性能得到明显提高,载荷的变化对复合材料的磨损量影响不大。

简介：介绍一种金属/合金的生产方法,用于恒电流和恒电位条件下由混合硫化物(Cu2S,NiS)生产Cu-Ni合金,称为直接电化学还原(DER)。研究槽电压和槽电流等工艺参数对还原得到的化合物组成的影响,以生产工业所需的CuNi10,CuNi20和CuNi30等合金。在1200°C下采用循环伏安法(CV)考察Cu2S和NiS在CaCl2熔体中的电化学行为。根据CV研究结果,Cu2S的阴极还原是一步完成的,即Cu2S?Cu;NiS的阴极还原则分两步进行,即NiS?Ni3S2?Ni。恒电流研究表明,在10A电流下电解15min,可制备出最高硫含量为320×10-6的高纯CuNi10合金。扫描电子显微镜以及能量色散X射线能谱和光学发射光谱(OES)测试结果表明,在2.5V电压下直接电化学还原15min,可制备出杂质含量低(即硫含量小于60×10-6)的所选成分的Cu-Ni合金。

简介：Themetal-organicchemicalvapordeposition(MOCVD)techniqueisapromisingprocessforhigh-temperaturesuperconductorYBa2Cu3O7-δ(YBCO)preparation.Inthistechnique,itisachallengetoobtainbariumprecursorswithhighvolatility.Inaddition,thepurity,evaporationcharacteristics,andthermostabilityofadoptedprecursorsinwholeprocesswilldecidethequalityandreproducibleresultsofYBCOfilm.Inthepresentreport,bis(2,2,6,6-tetramethyl-3,5-heptanedionato)barium(Ⅱ)(Ba(TMHD)2)wassynthesized,anditsstructurewasidentifiedbyFTIR,1HNMR,13CNMR,andESI-MSspectroscopy.Subsequently,thethermalpropertiesandthekineticsofdecompositionweresystematicallyinvestigatedbynonisothermalthermogravimetricanalysismethods.BasedontheaverageapparentactivationenergyevaluatedbytheOzawa,Kissinger,andFriedmanmethods,thevolatilizationprocesswasdiscussed,andallresultsshowthatBa(TMHD)2isunstableandhighlysensitivetothechangeoftemperatureduringthewholeevaporationprocess.Therefore,itisveryimportanttochoosesuitablevolatilizationtechnologyandconditionsforavoidingBa(TMHD)2break-down(orthermalaging)duringMOCVDprocess.Subsequently,thepossibleconversionfunctionisestimatedthroughtheCoats-Redfernmethodtocharacterizetheevaporationpatternsandfollowsaphaseboundaryreactionmechanismbythecontractingsurfaceequationwithaverageactivationenergyof118.7kJ.mol-1.

简介：在这份报纸，纺纱冰上的无磁性的Y离子的冲淡效果加重Dy2Ti2O7由红外线并且拉曼系列和磁化大小被调查。与温度弄软减少的异常声子在父母被发现并且冲淡除了之外，做的混合物，和Y能放松弄软声子233附近的红外模式?厘米<啜class=“a-plus-plus”>显示在纺纱冰材料联合的强壮的phononphonon的1,。当冲淡的水平不很高时，磁化大小表明无磁性的杂质严重地不处于扎根的状态影响纺纱冰规则。然而，大量冲淡提高混乱并且因为集体旋转扭动簇不再是可得到的，打破纺纱冰状态。

简介：通过基于密度泛函理论的第一性原理计算方法,对MgCu2,Mg2Ca和MgZn2的力学性能和电子结构进行计算,计算所得晶格参数与实验值和文献值相吻合。合金形成热和结合能的计算结果表明,MgCu2具有最强的合金形成能力和结构稳定性。计算了MgCu2,Mg2Ca和MgZn2的弹性常数,推导了体模量、剪切模量、弹性模量和泊松比。结果表明,MgCu2、Mg2Ca和MgZn2均为延性相,MgCu2的刚度最大,MgZn2的塑性最好。通过对结合能和弹性常数的计算,预测了MgCu2、Mg2Ca和MgZn2的熔点。通过对态密度（DOS）、Mulliken布居数、电子占据数和差分电荷密度的计算,分析了MgCu2、Mg2Ca和MgZn2的结构稳定性和力学性能机制。最后,计算和讨论了3种金属间化合物的Debye温度。