简介：Titaniumnitride(TIN)filmsweredepositedonAISI304stainlesssteelsubstratesusinghollowcathodeplasmaphysicalvapordeposition(HC-PVD).TitaniumwasintroducedbyerodingtheTicathodenozzleandTiNwasformedinthepresenceofanitrogenplasmaexcitedbyradiofrequency(RF).Thesubstratebiasvoltagewasvariedfrom0to-300Vandtheuniformityinfilmthickness,surfaceroughness,crystalsize,microhardnessandwearresistanceforthefilmwithadiameterof20mmwasevaluated.Althoughthecentralzoneoftheplasmahadthehighestiondensity,thefilmthicknessdidnotvaryappreciablyacrossthesample.Theresultsfromatomicforcemicroscopy(AFM)revealedalowsurfaceroughnessdominatedbyanisland-likemorphologywithasimilarcrystalsizeontheentiresurface.Highermicrohardnesswasmeasuredatthecentralzoneofthesample.Thesampletreatedat-200Vhadexcellenttribologicalpropertiesanduniformity.

简介：Nuclearbindingenergies,chargeradiiandthechargedistributionsofeven-eventin(Sn)isotopesarecalculatedusingrelativisticmeanfieldtheory,andthetheoreticalresultsarefoundtobeinaccordancewiththeexperimentaldata.ThenuclearchargeformfactorsforSnisotopesarecalculatedusingthephase-shiftanalysismethod.ItisshownthattheminimaofthechargeformfactorsshiftupwardandinwardwithanincreaseintheneutronnumberoftheSnisotopes.

简介：运用同步辐射X射线白光形貌研究了α-BaB2O4晶体内部的完整性并分析了α-BaB2O4晶体的缺陷行为及缺陷形成原因。在(001)面发现了生长扇界和亚晶界，而在(100)面和(120)面分别观察到了位错、位错组以及针状包裹体。运用白光形貌拍摄到高清晰的旁埃斑。

简介：Indiumtinoxide(ITO)transparentconductingfilmwastreatedwithoxygenplasmaimmersionionimplantation(PIII).X-rayphotoelectronspectroscopy(XPS)wasemployedtocharacterizetheeffect.Theresultssuggestedthattheoxygencontentinthesurfacewasincreasedandmaintainedformorethan50hcomparedwithtraditionalplasma-treatedsamples.Meanwhile,theworkfunctionofITOestimatedbycomparingthepeakshiftintheXPSdiagramsuggestedacorrespondingincreasebymorethan1eV.

简介：

简介：

简介：LiNdP4O12(LNP）晶体是一种新型的激光材料。本文报道了用同步辐射X射线白光形貌术和光学显微法研究由助熔剂籽晶旋转法生长的LNP晶体的生长缺陷，观察到了圆形生长台阶及精细的系列台阶结构，对晶体中的包裹物和位错缺陷等进行了详细的观察描述，还发现了一种比较奇特的腐蚀沟槽，分析了这种腐蚀沟槽的形成机理及各种缺陷的成因和克服办法。

简介：报道了用同步辐射X射线白光形貌术和光学显微法研究由助熔剂籽晶旋转法生长的LNP晶体的生长缺陷。本文除对晶体中的包裹物和位错缺陷等进行了详细观察描述外，还发现了一种比较奇特的腐蚀沟槽。最后分析了这些缺陷的成因和克服办法。

简介：

简介：

简介：

简介：

简介：

简介：

简介：采用XAFS方法研究浸渍法制备并于低温焙烧的CuO／γ-A12O3催化剂的局域结构。对于CuO负载量小于单层分散阈值的CuO／γ-A12O3(0．4mmol／100m2)，结果表明CuO物种是以层状分散的孤立原子簇存在于γ-Al2O3载体表面，其第一近邻Cu-O配位环境的结构与晶态CuO的相似，键长和配位数分别为0．195nm和4。对于CuO负载量等于单层分散阈值的CuO／γ-A12O3(0．8mmol／100m。)，已有少量的CuO纳米颗粒生成。对于CuO负载量大于单层分散阀值的CuO／γ-A12O3(1．2mmol／100m2)，其结构与多晶CuO的相近。基于CuO在γ-A12O33载体上的三种不同分散状态的结构特点，我们提出了CuO／γ-A12O3催化剂的结构模型。

简介：Theγ-Fe2O3nanoparticlescoatedwithDBSandCTABwerepreparedbythemicroemulsionmethod.Thecoatedsamplesshowenhancednonlinearopticalpropertiescomparedwiththeirbulkcouterpart.The.Moessbauerspectraatroomtemperatureweremeasuredforthecoatedferricoxides.Themonolayersoftheorganicmoleculearefoundtohaveastrongchemicalbondwiththesurfaceatomsandthushaveasignificantinfluenceontheelectronstructureofparticlesurface.@1999ActaMetallurgicaInc.

简介：ThetransientopticalpropertiesofnovelPbSnanoparticlescoatedwith2.6-O-diallyl-β-cyclodextrines(CDs)werestudiedbythefemtosecondpump-probetechnique.Theresultsshowthattheultrafasttransient-inducedabsorptionforthenovelcase.ComparedtothePbSnanoparticlesstabilizedwithpolyvinylalcohol(PVA),wefindthattheprocessforthenovelcaseisdifferentfromthePbS(PVA),WesuggestthattheCDssurfacemodificationcantrapholesonthesurfaceofPbSnanoparticles.ThiscaninduceanefficientchargeseparationbetweenthePbSnanoparticlesanditssurfaceandresultinanultrsafast-inducedabsorptionfornovelPbSnanoparticles.

简介：Thenanoparticlesγ-Fe2O3coatedwithsurfactants.DBS,STandCTAB.repsectively.weresynthesizedbymicroemulsionmethod.Thecoatedferricoxides.whichshowenhancednonlinearopticalpropertiescomparedwiththeirbulkcounterpart.wereprobedbyEXAFSinsolutionforms.Thex=-rayabsorptionspectraforFeKedgeweremeasuredatroomtemperaturebyhelpofsynchrotronradiationlightsource.Extendedx-rayabsorptionfinestructureanalysisshowsthatthecoatinglayersoforganicmoleculesinteractwithsurfaceatomsofnanopartices,theFe-Obondlengthwasextended.

简介：

简介：使用部分还原－共沉淀方法制备了平均粒径为3－11nm的球形Fe3O4纳米颗粒，以16：4：1的甲醇－乙醇－水混合溶液作为传压介质和均分散介质，利用金刚石对顶砧装置（DAC）研究了球形Fe3O4纳米颗粒的原位常温高压（0－31．8GPa)XRD谱和纳米颗粒的压致晶格结构变化。