简介：Cr2O3-formingferriticstainlesssteelshavebeenwidelyexploredasintermediatetemperaturesolidoxidefuelcells（SOFCs）interconnects.However,theevaporationofchromiascalemightmigratetoandpoisonthecathode,leadingtodegradationofthecellperformance.Inthisstudy,Ni-Co-Fe-Pcoatingsweredepositedontheferriticstainlesssteelbymeansofacost-effectivetechniqueofelectrolessmethod.Theyareexpectedtobeconvertedinto（Ni,Co,Fe）3O4spinelwithahighelectricalconductivityandCTEmatchwithstainlesssteel,whichcanblocktheevaporationofchromiaformedonsteelsubstrateexposedtothecathodeenvironmentoftheSOFC.TheeffectsofpH,massratioofFeSO4/（FeSO4+NiSO4+CoSO4）andtemperatureofsolutiononthedepositionrate,compositions,surfacemorphologiesandstructuresoftheNi-Co-Fe-Pcoatingswereinvestigated.TheresultsindicatedthatthedepositionrateincreasedwithincreasingpHwhenpHwaslowerthan9andthenreducedwhenpHwashigherthan9.Thedepositionrateincreasedwithincreasingtemperaturewhentemperaturewaslowerthan80℃andthendecreasedwhentemperaturewashigherthan80℃.ThedepositionratedecreasedwiththeincreaseinmassratioofFeSO4/（NiSO4+CoSO4+FeSO4）.ThecoatingsconsistedofNi,Co,FeandP.Thephasestructureofthecoatingwasamorphous.

简介：从制样方法及分析方法上对硅锰铁合金的分析方法进行了研究,采用定时、定压、定量制样、标准曲线制作等手段,主要对硅锰铁合金中Mn、Si、P等常规元素进行测定。对于X荧光光谱压片做了充分的前期准备工作,并对相关影响因素进行分析。该方法分析数据准确可靠,进而取得满意的分析结果。

简介：Advancedhighstrengthsteel(AHSS)hasbeenwidelyusedintheautomobileindustry.TheresistancespotweldingperformanceofDP980andQ&P980steelswasstudiedthroughcomparingthetwosteels'weldingcurrentrange,tensileshearstrength(TSS),crosstensionstrength(CTS),weldspots'microhardness,etc.Thefollowingconclusionswereachieved:ItiseasyforbothDP980andQ&P980steelstogetanuggetsizebiggerthan4mm,theyallhaveweldingcurrentrangesexceeding2kAandhighweldstrength.