摘要
ThehotductilityofFe-36NiinvaralloywithdifferentadditionsoftheelementceriumwasinvestigatedusingaGleeble-3800thermal-mechanicalsimulatoroverthetemperaturerange850-1050℃,andtheimprovementmechanismofthehotductilitywasanalyzedusingacombinationofSEM,EDS,andOM.TheresultsindicatedthatFe-36Niinvaralloyexhibitedpoorhotductilitybelow1050℃,whichwasmainlyattributedtoweakgrainboundariesandtheactionofgrainboundarysliding.However,thealloyswithceriumcontentsof0.016%and0.024%bothdemonstratedsubstantialimprovementinthehotductilityovertheentiretestingtemperaturerange.Theobservedimprovementofthehotductilityofthealloywith0.016%ceriumat950℃andthealloywith0.024%ceriumat900℃wasassociatedmainlywiththegrainboundarystrengtheningandtherestrictionofthegrainboundaryslidingbecausetheadditionofceriumreducedthesegregationofsulfuratgrainboundariesandrefinedthegrainstructure.Theoccurrenceandaccelerationofdynamicrecrystallizationwerefoundtoberesponsibleforthehighhotductilityofthealloywith0.016%ceriumat1000℃andthealloywith0.024%ceriumat950-1000℃asaresultoftherefinementofthegrainstructurebyadditionofcerium.
出版日期
2014年04月14日(中国期刊网平台首次上网日期,不代表论文的发表时间)