简介：目的纯镁表面采用超声微弧氧化技术，在电解液中添加AgNO3，探讨其对生物涂层组织及性能影响，为后续抗菌性和生物相容性试验提供实验基础。材料与方法电参数相同条件下，采用硅酸盐系镀液为对照组，在其基础上添加不同含量AgNO3为实验组，观察涂层表面和断面形貌、涂层相结构及成分分析，测定涂层结合力、摩擦系数和电化学腐蚀性能。结果添加AgNO3后，电解液导电能力增强，涂层表面微孔孔径增大，微弧数目减少，致密层更加致密，并有Ag新相产生。随着AgNO3含量增加，涂层结合力变大，摩擦系数变小，耐蚀性提高。结论添加AgN03后，涂层形成Ag新相，表面微孔孔径增大，致密层更加致密，提高了涂层结合力、耐磨性和耐蚀性。

简介：

简介：目的验证化学发光法检测第3代促甲状腺素(TSH-3)的性能。方法参照美国临床和实验室标准化协会(CLSI)的评价方法和国内文献,结合实际工作条件,设计验证方案,对西门子CentaurXP化学发光免疫检测系统测定血清TSH-3的精密度、准确度、分析灵敏度、分析测量范围、临床可报告范围以及生物参考区间等6个性能指标进行验证评价,并将检测结果与厂家提供的分析性能进行比较。结果TSH-3检测的批内和批间精密度分别为2.17%和2.14%,高、中、低三个浓度水平的日间精密度分别为7.98%、6.81%、6.69%;检测偏差在-3.45%～-1.55%;检测低限为0.0054μIU/ml,生物检测限在(0.0102～0.0153)μIU/ml,功能灵敏度约为0.0170μIU/ml;分析测量范围在(0.0054～140.6130)μIU/ml;临床可报告范围为(0.0153～703.065)μIU/ml;37份健康体检儿童中除2份标本结果在厂家提供的参考区间外,其余35份全部在参考范围内。结论化学发光法检测TSH-3在本室的分析性能与厂家提供的性能基本吻合,符合临床需求。

简介：目的探讨对氧化锆瓷层不同表面处理后,结合硅烷偶联剂的应用,通过人工老化实验,对比氧化锆瓷表面与复合树脂之间剪切粘结强度的影响,为临床应用提供依据。方法将120个试件随机分成酸蚀、喷砂、喷砂加酸蚀、空白组4组,各组再分为涂布硅烷偶联剂组和对照组,充填复合树脂2mm。经人工老化实验后,利用万能试验机对比其剪切粘结强度。结果氧化锆瓷层表面3种表面处理组,酸蚀并结合硅烷偶联剂组所获得的粘结强度最大,喷砂组其次,喷砂加酸蚀组最低。结论经过3种不同表面处理后,均能提高瓷层表面与复合树脂之间的粘结剪切强度,酸蚀组效果最佳。通过耐老化实验比较分析瓷表面应用硅烷偶联剂有利于提高瓷与复合树脂间的粘接强度。

简介：摘要：目的 深入探究中药炮制对中药药物性能功效及理化性质产生的影响。方法 收集于2019年9月-2020年9月来我院进行中医药治疗的120名患者资料，并分为对照组和实验组，对照组患者常规中药药物控制治疗，实验组患者中药炮制治疗，并对两组患者治疗效果进行对比。结果 通过研究发现实验组临床治疗总有效率为91.67%，对照组为75%，明显低于对照组。结论 中药炮制治疗可将药物的有效成分充分发挥出来，同时弱化其对患者器官产生的危害性反应，因此应该临床中广泛推广和应用。

简介：目的纯镁表面采用超声微弧氧化技术,在电解液中添加AgNO3,探讨其对生物涂层组织及性能影响,为后续抗菌性和生物相容性试验提供实验基础。材料与方法电参数相同条件下,采用硅酸盐系镀液为对照组,在其基础上添加不同含量AgNO3为实验组,观察涂层表面和断面形貌、涂层相结构及成分分析,测定涂层结合力、摩擦系数和电化学腐蚀性能。结果添加AgNO3后,电解液导电能力增强,涂层表面微孔孔径增大,微弧数目减少,致密层更加致密,并有Ag新相产生。随着AgNO3含量增加,涂层结合力变大,摩擦系数变小,耐蚀性提高。结论添加AgNO3后,涂层形成Ag新相,表面微孔孔径增大,致密层更加致密,提高了涂层结合力、耐磨性和耐蚀性。更多还原

简介：摘要目的观察研究根管治疗术后不同修复方式对牙根抗折性能的影响。方法收集我院口腔科正畸拔除的冠根完整的上颌第一前磨牙145颗作为研究对象，将牙齿分为A、B、C、D、E五组，每组29颗。A组为参照组，即完整离体牙，B组不进行修复，C组采用树脂充填修复，D组采用树脂嵌体修复，E组实施树脂充填联合固位纤维冠外保护。记录五组牙齿的破坏载荷值并加以对比分析。结果未修复患牙和树脂充填修复后患牙的牙根抗折性能远低于完整离体牙水平（P<0.05）；树脂嵌体修复和树脂充填联合固位纤维冠外保护后，患牙的牙根抗折性能接近完整离体牙水平（P>0.05）。结论对根管治疗术后的患牙实施嵌体修复和树脂充填联合固位纤维冠外保护，可以有效提高牙根的抗折性能，值得临床应用推广。

简介：摘要目的研究中药炮制对药物性能功效及理化性质的影响。方法选择地黄、马钱子与大黄三味中药，应用不同方法进行炮制。比较炮制前后的药物性能功效及理化性质。结果生大黄经炮制后变成熟大黄，其中的总多糖、梓醇、地黄苷A与地黄苷D均有所下降，药物性能与功效发生明显的改变，大黄炭的致泄效价不能进行检测，说明炮制会影响大黄的升降沉浮效果；士的宁是马钱子中的主要毒性成分，通过hplc法检测发现，马钱子经炮制后士的宁和马钱子碱含量明显降低；经炮制后大黄中的致泻价从炮制前的100%降低至45.18%。结论炮制后的中药，其药物性能功效、理化性质均会发生明显的变化，但药效与安全性却会提高，因此，要根据药物的实际使用情况选择合理的炮制方式，使其能在临床治疗中最大程度低发挥出应用的药用价值和治疗效果。

简介：目的研究两种纳米磁性氧化铁颗粒分别与骨髓干细胞（Bonemarrowstemcells，BMSCs）和脂肪干细胞（Adiposederivedstemcells，ADSCs）共培养时细胞对磁铁颗粒的摄取情况，以初步探讨其作为磁共振成像（MRI）对比剂去标记组织工程种子细胞而进行MRI示踪的可行性。方法制备粒径为6nm的Fe3O4磁性颗粒及经聚L-乳酸（PLLA）表面修饰的Fe3O4磁性颗粒（200nm），分别在细胞接种时及接种后24小时两种方式加入。使用电感耦合等离子体质谱（ICP—OES）检测细胞对铁颗粒的摄取量。结果细胞对铁颗粒的摄取量受纳米磁铁颗粒的种类，加入方式和细胞类型的影响。BMSCs和ADSCs对6nm粒径磁铁颗粒的摄取量显著高于对200nm铁颗粒的摄取量，而ADSCs摄取的量又高于BMSCs。结论6nm粒径的磁性氧化铁颗粒可以较好的被BMSCs和ADSCs吸收，具有良好的生物相容性，有望成为组织工程种子细胞的标记物来进行MRI示踪。

简介：　　【摘要】 目的 探讨分析中药炮制对药物性能功效及理化性质的影响效果。方法 66例同一种疾病使用中药治疗患者， 根据使用的药物是否进行了炮制将其分为对照组和观察组， 每组 33例。对照组患者采用未进行炮制的中药， 观察组患者采用进行了炮制的中药。比较两组患者治疗效果、治疗时间、毒副反应发生情况。结果 观察组患者治疗总有效率为 96.97（ 32/33）， 高于对照组的 81.82%（ 27/33）， 差异具有统计学意义（ P<0.05）。观察组患者治疗时间为（ 5.48±1.36） d， 短于对照组的（ 8.15±1.67） d， 差异具有统计学意义（ P<0.05）。观察组患者毒副反应发生率为 3.03%（ 1/33）， 低于对照组的 18.18%（ 6/33）， 差异具有统计学意义（ P<0.05）。结论 中药炮制对药物的药性具有一定的影响， 可以有效提高药效， 从而提高治疗效果， 缩短药物使用时间。其对中药的理化性质也有一定的影响， 可以减少药物对人体的毒副作用， 增加安全性。炮制是中药处理中不可避免的一环， 只有进行了合理炮制的中药才能更好的运用到临床治疗中去。  　　【关键词】 中药炮制 ;药物性能 ;理化性质 ;影响效果 ;回顾性分析  　 [Abstract] Objective To explore and analyze the effect of traditional Chinese medicine processing on the performance, efficacy and physical and chemical properties of drugs. Methods 66 patients with the same disease treated with traditional Chinese medicine were divided into control group and observation group, 33 cases in each group. Patients in the control group were treated with traditional Chinese medicine without processing, while patients in the observation group were treated with processed Chinese medicine. The treatment effect, treatment time and side effects were compared between the two groups. Results the total effective rate of the observation group was 96.97 (32 / 33), which was higher than 81.82% (27 / 33) of the control group, the difference was statistically significant (P < 0.05). The treatment time of the observation group was (5.48 ± 1.36) d, which was shorter than (8.15 ± 1.67) d of the control group, and the difference was statistically significant (P < 0.05). The incidence of adverse reactions in the observation group was 3.03% (1 / 33), which was lower than 18.18% (6 / 33) of the control group, and the difference was statistically significant (P < 0.05). Conclusion the processing of traditional Chinese medicine has a certain impact on the drug properties, which can effectively improve the efficacy, so as to improve the treatment effect and shorten the drug use time. It also has a certain impact on the physical and chemical properties of traditional Chinese medicine, which can reduce the side effects of drugs on human body and increase the safety. Processing is an inevitable link in the treatment of traditional Chinese medicine, only a reasonable processing of traditional Chinese medicine can be better used in clinical treatment.

简介：摘要目的研究在行根管治疗术患者中采取不同修复方式给牙根抗折性能带来的影响。方法参考不同修复方式将2014年8月至2017年8月期间本院收治的34例行根管治疗术患者进行分组，A组术后不修复（n=9例），B组术后树脂直接填充修复（n=8例），C组术后树脂嵌体间接修复（n=9例），D组术后树脂填充且实行固位纤维冠外保护（n=8例），观察A组、B组、C组、D组四组样本组间数据差异。结果数据研究显示，A组行根管治疗术患者的牙根抗折性能对比B组、C组、D组，统计学数据参考意义显著（P＜0.05）；D组行根管治疗术患者的牙根抗折性能显著低于A组、B组、C组，统计学数据参考意义显著（P＜0.05）。结论将不同修复方式应用于行根管治疗术患者均可获得显著作用，但树脂填充且实行固位纤维冠外保护更具优势。

简介：

简介：背景：普通剂型的左氧氟沙星在体内代谢快,半衰期短,纳米微球为解决这一问题提供了新的途径。目的：制备一种能够减少给药次数,维持平稳有效的血药浓度且能复合在组织工程支架材料上的左氧氟沙星聚乳酸-羟基乙酸共聚物[poly（lactic-co-glycolicacid）,PLGA]纳米微球。方法：采用乳化溶剂挥发法制备不同条件下的左氧氟沙星纳米微球。（1）取24只新西兰大白兔随机分为3组研究左氧氟沙星纳米微球的体内药代动力学特性,普通剂型组通过耳缘静脉注射普通剂型的左氧氟沙星注射液20mg/kg,未载药纳米微球组接受等剂量的未载药纳米微球,载药纳米微球组接受等剂量的左氧氟沙星纳米微球,每组8只。于定点时间测定静脉血中左氧氟沙星含量;（2）取45只新西兰大白兔建立尿路感染模型,随机分为3组,空白对照组每日经耳缘静脉注入生理盐水;传统剂型组注入普通剂型的左氧氟沙星（20mg/kg）;纳米微球组注入相应等剂量的左氧氟沙星纳米微球。于不同时间点行尿细菌培养,检测尿白细胞、血白细胞和中性粒细胞数;9d后行膀胱组织学检测评估左氧氟沙星纳米微球抗菌能力。结果与结论：（1）体内药代动力学特性：与传统剂型相比,最优条件下的左氧氟沙星PLGA纳米微球可以明显减少血药浓度的波动和给药频率;（2）抗菌性能评估：在每日用药的传统剂型组和仅一次给药的纳米微球组,兔感染症状逐步得到控制,在第9天时已基本治愈;此外,在相同时间点纳米微球组兔治愈数量基本高于传统剂型组,虽然只有在用药后的第5天两组之间差异有显著性意义;（3）结果表明：左氧氟沙星PLGA纳米微球抗感染能力强,缓释性能佳,能明显减少给药频次及延长作用时间,在治疗泌尿系统感染方面具有良好的临床和组织工程尿道应用前景。

简介：摘要:目的：是比较两种急性乙型肝炎药物病毒(HBV)之间荧光谱的定量pcr可以检测临床实验室和药物病毒试剂盒的实际临床应用性能。方法：主要是分别采用两种定量HBV在线荧光仪和定量pcr荧光检测的实验试剂盒,对526例的两个临床实验样品分别进行了荧光检测,比较两种实验试剂的检测灵敏度、检测结果的一致性及相关性。结果：两种试剂阳性一致性为97.44%,阴性一致性为95.77%,总一致性为96.77%,两种试剂具有较好的相关性,相关系数,r=0.965。结论：利用HBV一步法检验试剂本身不仅具有设备操作简单、定量准确、灵敏稳定性比较高等几大特点,是一种广泛用于医疗临床上对HBV快速进行定量精确检验的有效试剂。

简介：摘要：目的 对中和抑制时间分辨荧光免疫法（TRFIA）检测乙型肝炎病毒e抗体（抗-HBe）的性能进行研究。方法 应用中和抑制TRFIA检测抗-HBe。评价该方法学的检出限和定量限、准确度、精密度、参考品符合率、线性等分析性能指标。结果 检出限和定量限均为0.12 IU/mL；国家参考品符合率均能达到检定要求；重复性和实验室内精密度的变异系数（CV）均不高于15.0%；在0.12 IU/mL～3.20 IU/mL内，所有样本的实测浓度与理论浓度值的相对偏差均在±20%范围内，且相关系数均大于0.9800。结论 该方法学精密度好、线性范围宽、准确度高、参考品符合率高，能满足临床检测需要。

简介：摘要：目的：两种化学发光免疫分析系统检测促甲状腺素的性能分析。方法：选取院里2023年10月至2023年12月收治的100例样本，分别使用新产业MaglumiX8和罗氏Cobas-E601全自动化学发光仪进行TSH的检测，进行两个系统间TSH的方法学分析，对这两个系统的结果进行比对。结果：国产新产业MaglumiX8自动分析仪的TSH测试分析结果与罗氏Cobas- E601自动免疫分析仪水平符合性很高。结论：新产业MaglumiX8可满足临床对TSH的检测的要求，值得采用。

简介：摘要：目的：比较分析不同修复材料应用在口腔修复中的应用效果及抗摩擦性能差异。方法：抽选本院接诊口腔修复患者共81例为研究对象，设置对比性研究，病例纳入时间为2019年1月~2020年12月。根据患者口腔修复材料差异分组，对照组41例（陶瓷材料）、观察组40例（树脂材料）。比较两组口腔修复有效率、口腔功能改善效果及修复体不良预后发生率差异。结果：观察组修复治疗后3月有效率为100.00（40/40）、、6月有效率为97.50（39/40），治疗6月时观察组口腔语言功能评分为（16.52±2.05）分、咀嚼功能评分为（16.47±1.95）分，均高于对照组，P

简介：目的对钴铬合金进行植酸溶液浸泡处理，研究其耐腐蚀性及力学性能的变化，以便今后在临床上应用。方法将钴铬合金分别浸泡在不同pH值的植酸溶液中并浸泡不同的时间，然后取出再放入人工唾液中浸泡，检测腐蚀速率并观察表面形貌，以及进行拉伸、弯曲等力学性能检测。结果浸泡处理后钴铬合金的抗氧化性能较对照组有所提高，其力学性能也未发生明显变化。结论植酸可提高钴铬合金的耐腐蚀性能，并且对其力学性能无明显改变，处理方法相对简单，安全，且无毒无害，可以在临床上应用。

简介：

简介：摘要目的评价SysmexXN9000血液分析仪对外周血未成熟血小板比率（ImmaturePlateletFraction，IPF）的检测性能并建立本实验室的参考区间。方法使用SysmexXN9000检测IPF，统计其精密度、携带污染率、线性范围，通过IPF检测结果建立湘南地区参考区间。结果结论SysmexXN9000测定外周血IPF精密度、携带污染率、线性范围符合美国临床实验室标准化协会（NCCLS）的要求，并建立了本地区参考区间，可在本地区临床实验室推广应用。