简介：

简介：有关于30-50nm的谷物尺寸的nanocrystallineMg2Si(n-Mg2Si)的Densification行为被hot-pressing在显示的400°C.The结果调查n-Mg2Si的那个thedensification过程展出了三线性segments:p<0.3GPa，0.3GPa1.2GPa由Heckel决定了公式，在哪个之中在高压力范围p>1.2GPa的第三个快增加片断很少在常规纹理粗糙的polycrystallinematerials.Nevertheless被报导了，在调查的整个压力范围(0.125-1.500GPa)，n-Mg2Si的densificationbehavior能是Kawakita公式p/C=(1/a)描述的井有在对协议的起始的孔的好同意的constanta=0.452的p+1/(ab)。

简介：Basedonthedifferenceofhydroxygroupconfigurationondifferentplanesofα-Fe2O3nanoparticles,usingthespecialadsorptionandcoordinationofphosphateonthe(001)planeofα-Fe2O3,well-crystallizedandwelldispersedα-Fe2O3nanodiskswithdiameterof150–200nmandthicknessof40–80nmweresynthesizedviaahydrothermalmethod.Themagneticpropertiesofsynthesizednanodiskswereinvestigated.Itwasfoundthatthenanodiskspossessedasaturationmagnetization(Ms)of0.38emu/g,aremanentmagnetization(Mr)of0.031emu/gandacoercivityof452.91Oeatroomtemperature.TheMrandcoercivityofsynthesizedα-Fe2O3nanodisksarehigherandtheMsislowerthanthoseofotherpreviouslyreportedα-Fe2O3nanostructures.

简介：HfB2具有高熔点（3250℃）和高硬度（29GPa），成为颇具潜力的超高温材料。目前研究较多的是HfB2-SiC复合材料。主要介绍了HfB2-SiC复合材料的常用制备方法，包括热压烧结、放电等离子体烧结、化学气相沉积等，并展望了HfB2-SiC超高温材料的发展趋势。

简介：

简介：Fe-Ni-Almixturesashot-pressingsinteringadditivetoTitaniumdiboride(TiB2)werestudied.ItisfoundthatliquidalloyformedunderhightemperaturehardlyhaseffectsonthedensificationbehaviorsofTiB2-independent.Fe-Ni-AladditivejustworksasfillerbetweenTiB2particlesanddoesnotchangetheTiB2-independentsinteringbehaviors.PressingmodehasagreateffectontheliquidflowingbetweenTiB2particles.Multiple-stepspressingmodewillgivemoretimeandspacefortheliquidflowingandimprovetherelativedensityofTiB2-Fe-Ni-Alcermet.

简介：nano-TiO2粒子被液体水解作用方法准备并且描绘了使用XRD。它对二个代表的抗菌剂活动细菌，Escherichiacoli和葡萄球菌aureus，也被学习。试验性的结果出现了在600700瑵椠?楶牴?整瑳?湡?敲慰物?的nano-TiO2calcinated???業散挠污慶楲污搠晥'太B.吗？？

简介：

简介：

简介：

简介：MoleculardynamicssimulationusingauniversalforcefieldhasbeenemployedtodeterminethediffusioncoefficientsofO2andNa2SO4vaporintoB2O3andSiCfrom700Kto1273K,respectively.Einsteindiffusionwasobservedina250～300pssimulation.ThediffusioncoefficientfortheO2rangefromabout9.279×10-9cm2/sforB2O3to2.275×10-10cm2/sforSiCataloadingof32moleculespersimulationbox,thatfortheNa2SO4vaporrangefromabout9.888×10-7cm2/sforB2O3to1.837×10-10cm2/sforSiCataloadingof8moleculespersimulationbox.EnvironmentpropertiesofC/SiCcompositewillbeincreasedviatheB2O3preventingthediffusionofO2andNa2SO4vaporintothepyrolyticinterphaseandcarbonfibers.

简介：λ-MnO2waspreparedbycolumnmethodfromnormalspinelLiMn2O4withpurityof99.38%.TheinfluenceofLiMn2O4grainsizeandacidityofleachingsolutiononthelithiumleachingprocesswasstudied.TheresultsshowthattheappropriaterangeofLiMn2O4grainsizewas60-160meshesandtheconcentrationofleachingsolutionHClwas0.1mol·L-1.TheadsorptioncapacityQofλ-MnO2forlithiumincreasedwiththeincreaseofpHandchangedmarkedlyatpH6.0-10.0.Itwas3.80mmol/gatpH12.0.ThedistributioncoefficientsKdofLi+andNa+were3.406×104and2.300respectively,andtheseparationcoefftcientaLiNawas1.481×104atpH6.5.Asaresult,λ-MnO2isahighperformanceion-sievematerialforlithiumion.

简介：Asanodematerialsforlithium-ionbatteries,SiO_2isofgreatinterestbecauseofitshighcapacity,lowcostandenvironmentalaffinity.AfacileapproachhasbeendevelopedtofabricateSiO_2@Chollowspheresbyhydrolysisoftetraethylorthosilicate(TEOS)toformSiO_2shellsonorganicspheretemplatesfollowedbycalcinationsinairtoremovethetemplates,andthentheSiO_2shellsarecoveredbycarbonlayers.ElectronmicroscopyinvestigationsconfirmhollowstructureoftheSiO_2@C.TheSiO_2@ChollowsphereswithdifferentSiO_2contentsdisplaygradualincreaseinspecificcapacitywithdischarge/chargecycling,amongwhichtheSiO_2@CwithSiO_2contentof67wt%exhibitsdischarge/chargecapacitiesof653.4/649.6mAhg~(-1)over160cyclesatcurrentdensityof0.11mAcm~(-2).TheimpedancefittingoftheelectrochemicalimpedancespectroscopyshowsthattheSiO_2@CwithSiO_2contentof67wt%hasthelowestchargetransferresistance,whichindicatesthattheSiO_2@Chollowspheresispromisinganodecandidateforlithium-ionbatteries.

简介：ZrC涂层被低压力在石墨底层上扔有Br的化学蒸汽免职(LPCVD)2-Zr-C3H6-H2-Ar系统。微观结构和ZrC涂层的生长行为上的免职时间的效果被调查。ZrC涂层在一个岛层模式成长了。涂层的形成被ZrC的成核统治在起始20分钟，和快速的成核产生了ZrC的有细密纹理的结构涂层。免职时间什么时候在30min上，涂层的生长被统治由晶体，给安排列的结构。精力散X光检查光谱学证明到锆的碳的臼齿的比率在在ZrC涂层，和X光检查的1:1附近显示出的光电子光谱学ZrC是在涂层的主要阶段，由大约2.5mol%伴随了ZrO2次要的阶段。

简介：

简介：

简介：利用Stober方法合成了球形SiO2颗粒。在乙醇和水的混合溶剂中，以正硅酸乙酯（TEOS）为硅源、氨水作催化剂，在40℃水浴下制备SiO2球形颗粒。通过改变反应物TEOS以及催化剂氨水的加入量，制备了不同粒径的球形SiO2颗粒。利用扫描电镜（SEM）可以看出，随着TEOS和氨水加入量的增加，SiO2颗粒的粒径增大，并探讨了其变化机理。

简介：利用射频(RF)共溅射的方法在n-Si(111)衬底上,以SiO_2为主靶,上面放置不同数量的Si片和石墨片,沉积出掺杂氧化物SiC复合薄膜,随后在不同温度下进行退火处理,并研究了其光致发光谱和光激发谱。不同C含量的样品在450nm和580nm附近均得到不同强度的发光峰,主要来自于Si、C注入后引起的基质成键变化而带来的氧空位缺陷和Si晶粒,对于C含量较高的样品在580nm处观察到黄光发射与C团簇有关。利用FTIR和XRD表征了复合膜的结构,UV—VIS分光光度计表征了复合膜的透射吸收特征。

简介：Hydroxyapatite(哈，Ca10(PO4)6(哦)2)涂层被激光cladding技术在纯Ti(TA2)上制作。阶段结构，微观结构，microhardness和激光cladded的电气化学的行为哈在人工的身体液体的涂层被调查。HA涂层主要高度被创作的结果表演结晶哈。过渡的层在之间哈涂层和Ti底层被形成。Microhardness测量显示出逐渐地在过渡的层在TA2底层从150HVmicrohardness增加到600HV，并且由一减少到400HV在列在后面哈涂的层。电气化学的腐蚀测试证明HA涂层与TA2底层相比有更高开的电路潜力，更低的腐蚀水流密度和腐蚀率。

简介：介绍了纳米TiO2负载到ACF上的几种主要方法，分析了单一因素如：TiO2表面羟基含量、晶相组成、薄膜的晶粒尺寸、薄膜的厚度、TiO2／ACF比表面积等对TiO2／ACF吸附光催化净化空气性能的影响，对纳米TiO2与ACF相互作用增强净化效果进行了理论分析，为纳米TiO2与ACF复合方法及相互作用的理论研究和复合材料TiO2/ACF对净化空气的性能研究奠定了一定的基础。