简介:Thehotdeformationbehaviourof7075aluminiumalloyreinforcedwith10%ofSiCparticleswasstudiedbyemployingboth'processingmaps'andmicrostructuralobservations.Thecompositewascharacterizedbyemployingopticalmicroscopetoevaluatethemicrostructuraltransformationsandinstabilityphenomena.Thematerialinvestigatedwasdeformedbycompressioninthetemperatureandstrainraterangesof300-500℃and0.001-1.0s-1,respectively.Thedeformationefficiencywascalculatedbystrainratesensitivity(m)valuesobtainedbyhotcompressiontests.Thepowerdissipationefficiencyandinstabilityparameterswereevaluatedandprocessingmapswereconstructedforstrainof0.5.Theoptimumdomainsandinstabilityzonewereobtainedforthecomposites.Theoptimumprocessingconditionsareobtainedinthestrainraterangeof0.1-0.9s-1andtemperaturerangeof390-440℃withtheefficiencyof30%.
简介:ThehotdeformationbehaviorofextrudedAZ80magnesiumalloywasinvestigatedusingcompressiontestsinthetemperaturerangeof250-400℃andstrainraterangeof0.001-1.000s^-1.The3Dpowerdissipationmapwasdevelopedtoevaluatethehotdeformationmechanismsanddeterminetheoptimalprocessingparameters.Twodomainsofdynamicrecrystallizationwereidentifiedfromthe3Dpowerdissipationmap,