简介:Linearcontractionofgreyironsandcastings;Measurementandminimizationofresidualstressesinironcastings;Microstructurecharacterizationofductilethinwallironcastings;ProcessofManufacturingRiserlessCastingsfromHypereutecticHigh-StrengthIrons;Resources-SavingInoculationofHigh-QualityCastIrons;Thinwallcompactedgraphiteironcastings
简介:ApplicationofCastSimulationforLarge-SizedIronCastings,ApplicationofProtectiveFilmsandPenetrationPreventingPartingPowdersonGreenSandMoldsforIronCastings,Combinedhardeningoftheslidingguidewaysofthemetal-cuttingmachinetools,Computersimulationofvariousmethodsforgreensandfilling,Criticalityoffoundryimperfections,Effectofrapidsolidificationonslidingwearofironcastings.
简介:EffectsofappliedpressureduringfeedingonthefatiguepropertiesofcriticalcastaluminumalloycomponentsanAFS/CMCresearchprojectprogressreport,No.2;Effectsofshotblastingondimensionalvariationofcastings;Eliminatingfish-eyedefectsinductilecastings;Graphiteshapecharacterisationincastiron-fromvisualestimationtofractaldimension;intensificationofgraphitizmgannealinginmalleableironcastingsmanufacture。
简介:摘要:球墨铸铁件在铸造生产中经常出现缩松缺陷,若不能及时处理,铸件内部会出现大小不一的夹渣、疏松,严重影响铸件的外观质量和使用性能。为了提高球墨铸铁件质量,分析了缩松的形成原因及预防措施。首先分析了球墨铸铁的组织结构,认为碳化物、石墨是造成缩松缺陷的主要原因。在生产实践中发现:影响铸件缩松率高低的因素很多,如浇注温度、冷却速度等都会影响铸件的缩松倾向和程度。
简介:摘要:本文介绍了铸铁的焊接特性和焊接工艺的特点,及由此给电弧焊技术带来的难度。从铸铁电弧冷焊的焊接入手,在工作实践中,由于机床等常用设备老化及铸造方面的缺陷,造成铸铁件产生裂纹和断裂很多,需要采用相应的焊补工艺进行焊补。本文论述了灰铸铁电弧冷焊的焊接性及焊接工艺。例举了冲床机座(材质为灰铸铁 HT200)裂纹,采用纯镍焊条(Z308)电弧冷焊的实际操作过程和使用效果。
简介:摘要:详细介绍了灰铸铁件的质量检验,根据铸造缺陷的类别,综合分析其形生的原因并深入研究、探讨其相应的预防措施,对灰铸铁件的质量检验和铸造缺陷的预防有着一定参考价值。