简介：

简介：Thermodynamiccalculation,SEM(scanningelectronmicroscopy),TEM(transmissionelectronmicroscopy),XRD(X-raydiffraction),phaseextraction,andchemicalanalysiswereemployedtostudythephasestabilityandphaseprecipitationinanewNi-Cr-Cobasesuperalloyheat-treatedat704and760℃foralongtime.Theresultsshowthattheprecipitatesofthisnewalloyheat-treatedatstandardannealingconditionandheat-treatedat704and760℃foratimeupto2000hareγ′,MC,M23C6,andM6C,andηphaseformsatgrainboundariesandinmatrixofsamplesheat-treatedat760℃aswell.Themassfractionsofγ′(+η),MC,M23C6,andM6Cinallsampleshavenolargechangeswithanincreaseinagingtime,butγ′precipitatesgrowobviously.Theγ′-to-ηtransformationinthesamplesheat-treatedat760℃tookplacewithincreasingagingtime.TheηprecipitatesformaWidmanstattenpattemandtheγ′phaseshaveremeltedpartlyinthesamplesheat-treatedat760℃.Thealloymaintainsabettermicrostructuralstabilityduringprolongedagingat704℃,butaworsemicrostructuralstabilityduringprolongedagingat760℃.

简介：微观结构和形成的激光固体(LSF)的机械性质上的热处理的效果Ti-6Al-4V合金被调查。温度的影响和答案处理和老化处理的时间被分析。结果证明LSFed样品的微观结构与300μm的平均谷物宽度由Widmanstättenα板条和在圆柱的优先的β谷物针状的一些组成，它沿着免职方向(Z)从底层取向附生地成长。解决方案处理在处理主要影响的主要、第二等的α板条，和老化的宽度，方面比率，和卷部分上有重要效果主要α板条和宽度的方面比率和卷部分和第二等的α板条的卷部分。当样品是与答案处理对待的热时，球状的α阶段首先在LSFed样品被观察(950°C，冷却的8h/air(交流))或与答案处理(950°C，1h/AC)并且老化处理(550°C，在8h/AC上面)分别地。在热处理期间在LSFedTi-6Al-4V合金变粗和α阶段的globularization机制被介绍。为LSFedTi-6Al-4V合金获得好综合机械性质，优化的热处理政体被建议。