简介:TiO2nanoparticleswithdifferentphasesarepreparedbyhydrolysisoftitaniumtetrabutoxideinthepresenceofHCl.ThecompositionandmicrostructureoftheresultingsamplesarestudiedbyXRDandTEM.TheseresultsshowthattherangeofparticlesizeofTiO2isfrom20to30nm.ThemechanismofTiO2photocatalysisreactionhasbeendiscussedextensively.PhotocatalyticactivitiesofnanometerTiO2arealsoevaluatedbydegradationofthecrystalvioletsolution.ExperimentalresultsindicatethatthesynergisticactionofH2O2andultrasonicwavegreatlyenhancesphoto-catalyticreactionofTiO2.
简介:Iron(Ⅲ)-dopednanostructureTiO2-coatedSiO2(TiO2/SiO2)particleswerepreparedusingthelayer-by-layeras-semblytechniqueandtheirphotocatalyticpropertywasstudied.TiO2colloidsweresynthesizedemployingthesol-gelmethodwithTiCl4asaprecursor.ThesampleswerecharacterizedbyFouriertransforminfraredspectroscopy(FTIR),SEM,EDS,XPS,andXRD.TheexperimentalresultsshowthatTiO2nanopowdersonthesurfaceofSiO2particlesarewelldistributed,theamountofTiO2isincreasedwiththeaddingofcoatinglayers,thepureanatase-TiO2coatinglayersaresynthesizedat500°C,andthephotocatalyticactivityofFe3+-dopedTiO2/SiO2ishigherthanthatofundopedTiO2/SiO2.
简介:Nb-24Ti-18Si-2Al-2Hf-4CrandNb-24Ti-18Si-2Al-2Hf-8Cralloyswerepreparedbyarcmeltinginawater-cooledcrucibleunderargonatmosphere.Microstructuralcharacteristicsandoxidationresistanceofthealloysat1250℃wereinvestigated.Theresultsshowthat,whentheCrcontentis4at%,themicrostructuresconsistof(Nb,Ti)_(ss)andNb_5Si_3;asCrcontentincreasesto8at%,C14LavesphaseCr_2Nbisformed.Theisothermaloxidationtestsshowthattheoxidationkineticsofthetwoalloysfollowsimilarfeatures.Theweightgainsofthetwoalloysafteroxidationat1250℃for100hare235.61and198.50mg·cm~(-2),respectively.Duringoxidation,SiO_2,TiO_2,Nb_2O_5andCrNbO_4areformedatfirst.Then,Ti_2Nb_(10)O_(29)isformedafteroxidationfor20minandbeginstochangeintoTiNb_2O_7astheoxidationproceeds.SiO_2isformedassolidstateatfirstbutlaterevolvesintoglassystatetoimprovethecohesionofthescale.Afteroxidationfor100h,oxidationproductsconsistofSiO_2,TiNb_2O_7,Nb_2O_5andCrNbO_4.
简介:ElectrocrystallizationMechanismofTungsteninMoltenKF-B_2O_3-K_2WO_4WenZhenhuanandLiGuoxun文振环,李国勋(GeneralResearchInstiiuteforNo...
简介:介绍一种金属/合金的生产方法,用于恒电流和恒电位条件下由混合硫化物(Cu2S,NiS)生产Cu-Ni合金,称为直接电化学还原(DER)。研究槽电压和槽电流等工艺参数对还原得到的化合物组成的影响,以生产工业所需的CuNi10,CuNi20和CuNi30等合金。在1200°C下采用循环伏安法(CV)考察Cu2S和NiS在CaCl2熔体中的电化学行为。根据CV研究结果,Cu2S的阴极还原是一步完成的,即Cu2S?Cu;NiS的阴极还原则分两步进行,即NiS?Ni3S2?Ni。恒电流研究表明,在10A电流下电解15min,可制备出最高硫含量为320×10-6的高纯CuNi10合金。扫描电子显微镜以及能量色散X射线能谱和光学发射光谱(OES)测试结果表明,在2.5V电压下直接电化学还原15min,可制备出杂质含量低(即硫含量小于60×10-6)的所选成分的Cu-Ni合金。
简介:本文采用磁粉、X射线、CT和超声等无损检测和金相分析等方法对40CrNi2Si2,MoVA钢制零件的磁痕显示进行了系统分析。研究认为,40CrNi2Si2MoVA钢制零件的磁痕显示为显微成分沿变形方向偏析导致的马氏体转变点Ms差异所致。显微成分偏析是钢锭结晶过程中不可避免的,但可通过优化熔炼工艺参数降低显微偏析的程度。本文还分析了四种磁痕显示的类型及其判别方法。