简介:铁镍基合金Incoloy825在焊接时容易出现热裂纹和气孔等缺陷;当在容器制造中受到不正确的加热(中温敏化)后,使用在某些介质中可能产生晶间腐蚀。缺陷的产生与原材料和焊接工艺有直接关系。在原材料方面应控制母材的化学成分和选择合适的焊材;在焊接工艺方面,焊前应保证母材和焊材干净,焊接过程中高温熔池和焊缝应得到有效保护,控制焊接参数,减小线能量,减少焊接接头在中温的停留时间。
简介:Widegapbrazing(WGB)experimentsusingthebuttedspecimenwitha1.5mmgapwerecarriedoutfortherepairofthefailedK418Bsuperalloylow-pressureturbinevanes.Thehightemperaturecreeprupturestrengthsofthebrazedjointsweretested,andthemicrostructuresandfracturesurfacesofthejointswereobserved.TheresultsshowthatthemicrostructureofK418Balloyjointiscomposedofdenseequiaxedgrain,smallanddiscretecompoundswithafewmicro-pores.Duringthecreeprupturetest,thecracksinitiatepreferentiallyatthemicro-poreorthegrainboundary,thenpropagatealongthegrainboundarytillthefracturehappens.Thecreeprupturestrengthat700℃ofthebrazedjointswith50%brazemetalintheworkingpartcouldexceed90%thatoftheK418Bsuperalloy,andthejointswith100%brazemetalintheworkingpartachieve70%to80%ofthecreeprupturestrengthsfortheK418Bbasemetal.
简介:Duetothedisturbancesofspatters,dustsandstrongarclight,itisdifficulttodetectthemoltenpooledgeandtheweldlinelocationinCO2weldingprocesses.Themedianfilteringandself-multiplicationwasemployedtopreprocesstheimageoftheCO2weldinginordertodetecteffectivelytheedgeofmoltenpoolandthelocationofweldline.TheB-splinewaveletalgorithmhasbeeninvestigated,theinfluenceofdifferentscalesandthresholdsontheresultsoftheedgedetectionhavebeencomparedandanalyzed.TheexperimentalresultsshowthatbetterperformancetoextracttheedgeofthemoltenpoolandthelocationofweldlinecanbeobtainedbyusingtheB-splinewavelettransform.Theproposededgedetectionapproachcanbefurtherappliedtothecontrolofmoltendepthandtheseamtracking.