Thetungsten-inert-gas(TIG)arcweldingexperimentsofcementedcarbideYG30andsteel45werecarriedoutusingtheNi-Fe-Cfillingalloys.Theetaphasesandmechanicalpropertiesofweldedjointswereanalyzedbymeansofscanningelectronicmicroscope(SEM),transmissionelectronicmicroscope(TEM)coupledwithselecteddiffraction,electronicprobemicroanalysisandbendingstrengthmethods.Theexperimentalresultsshowthatthechemicalcompositionofthefillingalloysaffectsetaphaseformation.Whenthecarbonandnickelcontentsinfillingalloysare0.61wt%and55.29wt%,respectively,noetaphasesform.Andthejointbendingstrengthisthehighestto1.352GPa.Butiftheyare0.01wt%and55.38wt%,theetaphasesareformedattheboundariesofthecementedcarbideandtheweld,andthethicknessofetaphaselayerisabout110micrometers.Andthejointbendingstrengthislow.Usually,theseetaphasesareanomalouslygranular,andeasytoaccumulateattheboundariesbetweencementedcarbidesandtheweld.TheyaremultipleM6Crichintungstenandiron.