简介：SiliconoxynitridewasaddedinshapedAl2O3-SiC-Crefractorymaterialtoimprovetheslagresistanceinthispaper.Optimumaddingquantityofsiliconoxynitridepowderwasalsostudied.TheresultsshowthattheslagresistanceofAl2O3-SiC-Cshapedrefractoryisimprovedwhen2%or3%Si2N2Oisadded.AreasonableamountofSi2N2OaddedintoAl2O3-SiC-Cshapedrefractorycanproducesiliconoxideintotheslag,whichcanimprovetheviscosityofslagandpreventtheslagerosionandpenetration.

简介：ThepaperdescribestheeffectofadditivesAl,Si,SiCandB4ContheexpansionofMgO-ZrO2-Cmaterialafterbeingcoked.TheresultsindicatethatAlandSicannotincreaseitshotandcoldstrength.AlandSiwereoxidizedtoformAl2O3andSiO2respectively,andthenreactedwithCaZrO3orstabilizerinc-ZrO2toformcalciumaluminate,spinel(MA),dicalciumsilicate(C2S)andforsterite(M2S).Meanwhile,α-C2Swastransformedtoγ-C2Sandc-ZrO2tom-ZrO2whentemperaturechanged.AlltheabovereactionsresultedinthedecreaseoftheamountofAl4C3andSiCandtheincreaseinbulkvolume,whichcausedthestructureofMgO-ZrO2-Cmaterialdestroyed.Hence,contrarytotheMgO-Cmaterial,whenaddingAl.andSi,theMgO-ZrO2-Cmaterialwouldbestructurallydeterioratedafterheat-treatmentanditsstrengthandcorrosionresistancedecreased.

简介：

简介：Zirconiagraphiterefractoryisusedasacore-nozzleinthethin-stripcastingofsteel.Post-mortemanalysisofusedrefractorywasperformedinanefforttoestablishthefailuremechanism.CorrosionbehaviorwasstudiedagainstmoltensteelwithMnO-SiO2basedliquidinclusions.CorrosionofthesematerialsinvolvesdissolutionandoxidationofgraphiteinthematrixfollowedbypenetrationofliquidslagleadingtodegradationofZrO2particles.Thermodynamicequilibriumcalculationswereperformedtostudythiscorrosionmechanism.

简介：

简介：Bao-HitachiMetalRoll(NanTong)Co.,Ltd.onProductionTheconstructioncompletionandproduction-onceremonyofBao-HitachiMetalRoll(NanTong)Co.,Ltd.investedandestablishedbyBaosteelandJapanHitachiMetalwasheldon24thOctober.Bao-HitachiMetalRoll(NanTong)Co.,Ltd.issetbyjointventureofUSD65millioninvestedbyBaosteelandHitachiMetal,theconstructionstartedinSeptemberof2006.TrialproductionstartedonthebasisofcompletionofequipmentcombinedtestinAprilof2006.Theplantaimsatworldwidethinstriphotrollingplantsaspotentialclientsandprovideshighqualityhotrollingmillworkrollsproducedwithcentrifugallycastandstaticcast,etc.Accordingtotheschedule,themonthlyou

简介：

简介：

简介：Simplethree-pointbendingtestatambienttemperaturecharacterizedthemechanicalbehaviorofburnedAl2O3-Crefractoriesbeforeandafterthermalshockinassociationwiththeprocessingparameters(graphitecontentandcokingtemperature,etc.).Theresultsshowedthatnon-linearplastic-elasticbehaviorunderloadlowerthancoldmodulusofrupture(CMOR)wasregisteredinallspecimensandreallinearelasticbehaviorcouldbeidentifiedafterthefirstload.Thetotaldeformationcouldbedividedintotwoparts,plasticandelasticareas.ThegraphitecontentandjointbondingsystemofcarbonandceramicphaseswereresponsibleformechanicalbehaviorofAl2O3-Crefractories.

简介：

简介：Inthisstudy,inordertoevaluatetheperformanceofhomogenizedbauxite,twoAl_2O_3-SiC-Ccastableswerepreparedusinghomogenizedbauxiteandbrownfusedcorundumasaggregates,respectively.5mass%andalusitewasintroducedintothetwocastablessoastoresearchtheeffectandmechanismofandalusiteinAl_2O_3-SiC-Ccastables.Theresultsshowedthat:(1)comparedwiththebrownfusedcorundumbasedcastables,thehomogenizedbauxitebasedcastableshadhighercoldstrengthafterheattreatment,butlowerhotmodulusofrupture;(2)additionof5mass%andalusitecouldenhancethecoldandhotmodulusofrupture,improvethethermalshockresistance,andoptimizethemicrostructureofspecimens;(3)themullitizationofandalusitewasnotobviousinthecastablesfiredat1100-1400℃.

简介：

简介：ThispapertestifiesthataluminiumandsiliconaswellastheircarbidexandnitridescanreactwithCOincarbon-containingzonetoformAl2O3andSiOgasthroughexperimentandthermodyanmicanalysis,ThegasesdiffusetooxidizedzoneandreactwithoxidizerssuchasCO2,Asaresult,Al2O3andSiO2aredepositedfromthegases,wihichblockthepores,thusreducetheamountofgasdiffusionandincreaseoxidationresistnaceofcarbon-containingmaterials.

简介：

简介：Theroleofnano-SiO2andultra-fineboroncarbideonthepropertiesofalumina-graphitematerialswasinvestigated.Thestudyshowedthattheultra-fineboroncarbideaddedmodifiedthemicrostructureofresidualcarbonandpromotedthechemicalbondbetweenresidualcarbonfromphenolicresinandflakegraphite.Thecarbonwhitecouldstrengthentheresidualcarbonfromphenolicresin.ThesetwoadditivesimprovedthemechanicalpropertiesofAGrefractoriesatbothroomtemperatureandhightemperature,andthermalshockresistancewasimprovednoticeably.Whenthetwoadditivesweredopedtogether,carbonwhitecouldretardtheevaporationofB2O3.Thermalshockresistancewasguaranteedwithasmalleramountofultrafineboroncarbide.

简介：Thepotentialapplicationsofsomehightenologiesinrefractories,suchas,nanotechnology,in-situsynthesis,self-propagatinghigh-temperaturesynthesis,functionalgradientmaterials,computerassisteddesignandsomenewadvancedrefactoriesinSi-Al-O-Nsystemarebrieflydescribed.Thecharacteristicsandpreparationprocessesofthesenewrefractoriesareintroduced,andtheremainingproblemsawaitingeffectivesolutionsarepointedout.Somesuggesionsonfuturediectionofresearchanddevelopmentarefitlymade.

简介：TheeffectofTi(C,N)onpropertiesoflow-carbonMgO-Cbrickswasinvestigated.Thephasecompositionandthemicrostructureofthematrixoflow-carbonMgO-CbrickcontainingTi(C,N)werestudiedbyXRDandSEManalysistogetherwithEDS.TheresultsshowedthatTi(C,N)distributedinthematrixoflow-carbonMgO-Cbrickuniformlyafterbeingtreatedat1600℃for3hincokepowderbed,andTi(C,N)andMgOformedasolidsolution.Afterthetreatmentat1600℃for3hincokepowderbed,thebulkdensityandcoldcrushingstrengthoflow-carbonMgO-CbrickwithTi(C,N)decreased,andtheapparentporosityandlinearchangerateofspecimensincreased.Theoxidationresistanceoflow-carbonMgO-CbrickwithTi(C,N)wassuperiortothatoflow-carbonMgO-Cbrickwithnoadditives,butinferiortothatoflow-carbonMgO-CbrickwithAlpowder.TheslagresistanceofthespecimenwithTi(C,N)wasexcellentaswell.

简介：

简介：

简介：Sillimanite,kyaniteandandalusiteareadvantageousnaturalrefractoryrawmaterialsforaluminosilicaterefactoriestoattainimprovedkeyproperties.Thispaperaredividedintopartstointroducetheirresourceandtechnicalcharacteristicinthefirstpart,andtheirapplicationsinrefractoriesinthesecondaprttobesucceeded.Inthispart,basedonauthors'knowledgeandsources,informationontheirreserve,distribution,compositionandcharacteristicisprovided,tobringittolightthatChinaisrichinthereserveofthem,inparticularandalusite.Thesillimanitegroupmineralsarecharacterizedbytheirphasetransformationtoformprimarymulliteandsecondarymullitewhenaddedinhighaluminasystem,accompaniedbyvolumeexpansion,whichcanbetakenusetoimprovecreepresistancesandthermalshockresistanceoftherelatedrefractories.